ABSTRACT A frequent problem, whose solution requires a scientific approach due to its phenomenological essence, is cracking in aluminum joints. The causes of cracking in 3003 aluminum joints by Gas Metal Arc Welding (GMAW) are defined in this research. The study was carried out on actual joints in a food product container. A refrigerated disk was used for extracting the sample, trying not to alter the material to maintain evidence of possible causes of failure. Macrograph of the welded joints, and visual inspection, chemical analysis by optical emission spectrometry, stress testing of base material analyzes were performed to the joint sample. It is conclude that the lack of fusion and penetration is the cause of cracking, which act as stress concentrations and they were originated by deficiencies when carrying out welding.

RESUMEN El agrietamiento en uniones de aluminio constituye un problema frecuente cuya solución requiere un enfoque científico dada su esencia fenomenológica. En el presente trabajo se determinan las causas del agrietamiento en uniones de aluminio 3003 por soldadura GMAW (gas metal arc welding). El estudio se realizó en uniones reales de un contenedor de productos alimenticios. La muestra se extrajo con disco refrigerado, cuidando no alterar el material para mantener las evidencias de las posibles causas de falla. A la muestra de la unión le fueron realizados los análisis siguientes: inspección visual, análisis químico por espectrometría de emisión óptica, ensayo de tensión del material base y macrografía de las uniones soldadas. Se concluye que la causa del agrietamiento tiene su origen en la falta de fusión y penetración, que actúan como concentraciones de tensión y que fueron originadas por deficiencias en la ejecución de la soldadura.

This research deals with a study to determine the cause of cracking and later broke of an accessory made of stainless 316 steel in the cooling circuit of a reactor. Several characterization techniques were applied such as: optical emission spectrometry, sweep optical and electronic microscopy, including microanalysis with EDAX. It was concluded that the main cause of the failure are related to a mixing deterioration mechanism by intercrystalline corrosion sensitive, mechanic fatigue and stress corrosion cracking.

El artículo aborda un estudio para determinar la causa de agrietamiento y la posterior rotura de un accesorio fabricado de acero inoxidable 316 en el circuito de enfriamiento de un reactor. Para ello, se le aplicaron varias técnicas de caracterización, como espectrometría de emisión óptica, microscopia óptica y microscopía electrónica de barrido, incluyendo microanálisis con zonda EDAX. Se concluyó que la causa raíz de falla se vincula a un mecanismo mixto de deterioro por sensibilización a la corrosión intercristalina, corrosión bajo tensión y fatiga mecánica.

The presence of acicular ferrite (AF) in the microstructure of weld bead, in a specified range of values, increase considerably the toughness of welded joints. The present paper, for that reason, study the relationship between the acicular ferrite quantity in the deposited metal and the oxygen present in the active gas mixture of CO2+O2, during the execution of butt welded joints with straight edges, in low carbon steels with consumable electrode and gas protection (GMAW) in invariable conditions of process parameters (welding current, arc voltage, welding speed, electrode extension, and gas flow). The graphic relation between the acicular ferrite and the oxygen content was established, as result of the research work.

La presencia de ferrita acicular (FA) en la microestructura del cordón de soldadura, dentro de determinado rango de valores, eleva considerablemente la tenacidad de las uniones soldadas. Es por ello, que el presente trabajo trata sobre un estudio que relaciona la cantidad de ferrita acicular en el cordón en función del contenido de oxígeno presente en la mezcla activa CO2+O2, durante la realización de uniones soldadas de bordes rectos en aceros de bajo carbono con el proceso con electrodo fusible y protección gaseosa (GMAW) en condiciones invariables de parámetros de proceso (corriente de soldadura, voltaje de arco, velocidad de soldadura, longitud libre y flujo de gas protector). Como resultado del trabajo se estableció la relación gráfica existente entre la ferrita acicular y el contenido de oxígeno en la mezcla.